A low density gypsum based (with no mineral fibres), machine applied fire protection system. It is a cost effective and fast application system for the fire protection of steel and concrete structures. It bonds tightly to steel and concrete substrates, forming a hard surface which does not spall, dust or flake. Being gypsum based, is not designed for continuous exposure to weather or water.

 

Features and benefits:

 

  • Longevity- if undisturbed, Monokote is designed to last for the life of the building.
  • Proven in-place performance- it will stay in place during construction phase, for the life of the building until the day of the fire and meanwhile the intervention of the fire fighters.
  • Safety- monolithic barrier with no joints and do not need a chemical reaction.
  • Thin system- no need to allow the room between steels and over-cladding for expansions that is required for intumescent coating.
  • Low density- less net weight applied on the structures.
  • Value for money- direct application on unprimed steel with no corrosion pre-treatment in a controlled environment in a C1 (BS EN ISO 12944-2:1988).
  • Program benefit- installation to start as soon as the concrete deck of the floor above is poured.
  • Building Code compliant- ICBO, SBCCI, BOCA and ICC.
Platform Compatible Version Certified to
IFC IFC - 1 2.1
Revit Revit - 1 2.1

  • Properties and values
  • More BIM objects

Properties and values

COBie
BOS_General
NBS_Data
AbrasionResistance
8.3 cm³
AirErosion
0.000 g/ft² (0.00 g/m²)
Applications
Shall not be used if it contains partially set, frozen or caked material, The minimum average density shall be that required by the manufacturer, listed in the UL Fire Resistance Directory for each rating indicated, ICBO Evaluation Report, as required by the authority having jurisdiction, or minimum average 15 lbs/ft3 (240 kg/m3), whichever is greater, monokote shall be mixed with water at the job site, to be used with Monokote Fireproofing* to enhance set characteristics and product yield, the Monokote Accelerator is injected into the Monokote Fireproofing at the spray gun, monokote Accelerator shall be mixed and used according to manufacturers recommendations, applied directly to the steel, at various rates of application which will be job dependent
BondImpact
No cracking, spalling or delamination
BondStrength
339 psf (16.2 KPa)
Combustibility
Less than 5 MJ/m² total, 20 kw/m² peak heat release
Components
n/a
Compression
1,483 psf (71.0 KPa)
Corrosion
Does not contribute to corrosion
Deflection
No cracking, spalling or delamination
DryDensity
15 pcf (240 kg/m³)
HighVelocityAirErosion
No continued erosion after 4 hours
ImpactPenetration
3.9 cm³
Mix
n/a
ResistanceToMoldGrowth
No growth after 28 days
Storage
All material to be used for fireproofing shall be delivered in original unopened packages bearing the name of the manufacturer, the brand and proper UL labels for fire hazard and fire resistance classifications, material shall be kept dry until ready for use, packages of material shall be kept off the ground, under cover and away from sweating walls and other damp surfaces, all bags that have been exposed to water before use shall be discarded, stock of material is to be rotated and used before its expiration date